Good quality PFC-20 Synthetic Fiber Polyester Resin Wear rings stocked compound manufacturer

Type Wear Rings
Application Automotive industry
Supply Ability 10000
Payment Terms TT , LC , Others
Tags:

Detail

Color: Green
Impact Strength: 105 J/m
Temperature: -40° to 130° C, -40° to 266° F

PFC-20 Synthetic Fiber Polyester Resin Wear rings

Wear rings prevent metallic contact between pistons and cylinders or rods and glands where forces act perpendicular to the direction of movement.

PFC-20 Material Structure: 

Polyester resin + synthetic fiber

PFC-20 is composed of synthetic fiber, reinforced polyester resin and self-lubricating micro powders. PFC-20 features in low friction, high mechanical property, good corrosive resistance and low water absorption.

PFC-20 Material Technical Parameters:


Part Number PFC-20 Test Method
Color Green /
Density 1.2-1.4g/cm³
0.043-0.051lb/in³
DIN 53476
Tensile Strength 60MPa
8700PSI
ISO 527
Ultimate Compressive Strength 320MPa
46400PSI
ISO 604
Impact Strength 105 J/m /
Rockwell Hardness 80HRM ASTM D-229
Coefficient of friction 0.14-0.18(Dry)
0.08-0.11(Oil)
ASTM D 1894
Temperature -40° to 130° C
-40° to 266° F



Wear Cut Styles:




Advantages
Angle cut rings improve bearing stress at the gap. These rings tend to suit reciprocating movement.
Straight Cut, also known as Butt Cut rings are the easiest style to install in many applications. Straight cut rings are best suited for rotary movement.
Step cut rings also improve bearing stress at the gap. However, they offer better resistance to contaminants and spike loads. This type of design offers the best level of performance.


Typical application:

Guide rings

Bearings, Shaft sleeves, Bearing Bushes

Shipbuilding, Marine Components

Engineering Machinery Components

Hydroelectric Power Components


Standard Size Sheet, additional sizes are available upon request.

Download PDF: PFC-20 Synthetic Fiber Polyester Resin Wear Rings.pdf